Technical Parameter：
Chemical Composition | C | Si | Mn | P | S | Cr | W | Ni | Fe | N |
0.05-0.15 | 0.4 | 1-1.2 | 0.04 | 0.03 | 19-21 | 14-16 | 9-11 | 3 |
|
|
|
|
|
|
|
|
|
| ASTMF 1907 |
Basic information:
L-605 alloy is a high-performance cobalt-based superalloy with good physical and mechanical properties, thermal expansion, electrical properties and biocompatibility, and usually requires the use of special processes and equipment for processing, such as cutting, hot forming, welding and so on.
Applicable standards:
Europe | USA | Other |
| ASTMF 1907 | 1S05832-5 |
Mechanical properties:
Physical constants and thermal properties
Density | 9,27 g/cm³ |
Melting point | 1330 - 1410 °C |
Thermal conductivity | 9,4 W/m · °C |
Coefficient of expansion at 21 - 93°C | 13 μm/m · °C |
Typical mechanical properties (room temperature)
Yield strength | min. 460 MPa |
Tensile strength | min. 1000 MPa |
Elongation | min. 50% |
Medical application product range:
L-605 alloy has good biocompatibility and corrosion resistance, and it is widely used in the manufacture of medical devices such as artificial heart valves and vascular stents, as well as other types of implants such as artificial joints.